1, use: one-component silicone glass can use instant glue, glue gun is very easy to hit it from plastic bottles, and use the spatula or wood trim its surface.
2, sticking to the time: silicone rubber curing process is from the surface to inner development, different characteristics of the silicone table dry time and curing time is different (details please refer to the fourth article of curing time of the technical parameters of content), so if you want to repair was carried out on the surface must be conducted before the glass glue dry table (acid gel, neutral cellophane tape shall generally be in 5 to 10 minutes, neutral mixed glue shall generally be in 30 minutes). If the color paper to cover a certain place, glue, must be removed before epithelialization.
3, cure time: glass adhesive curing time is as the adhesive thickness increases, such as 12 mm thickness of acidity glass glue, may take 3 to 4 days can be solidified, but about 24 hours, have 3 mm outer layer has formed. Most bonding glass, metal or wood, after 72 hours at room temperature is 20 pounds per inch of the peel strength. If use some or all of the sealed glass glue, so, cure time is determined by the degree of closed tightly. In absolute airtight place, it may never keep curing. If the temperature will make glass glue is soft. Metal and metal bonding gap should not be more than 25 mm below. In all kinds of adhesive, including closed cases, after bonding equipment before use, should be fully check the bonding effect.
Acidity glass glue in the process of solidification, due to the volatilization of acetic acid will produce a taste, the taste will disappear in the process of curing, after curing will no peculiar smell.
4, adhesive: a. wiping the metal and plastic surface completely, degreasing, then in addition to plastic surface with acetone rinse all first, rubber surface application of sand paper burnish, then wipe with acetone. The use of acetone please abide by the use of the matters needing attention of the solvent. B. glass glue evenly coated on the surface of the object that is ready, if is two surface bonding, can put a look for the position, the other side extrusion with enough force to squeeze out the air, but be careful not to squeeze out the glass glue. C. puts the device of the adhesive at room temperature, glass glue curing.
5, seal: to use silicone glass glue sealing occasions, also carried out in accordance with the above steps, glass glue hard into joint or crack, make good contact with glass glue and surface.
6, cleaning: glass glue before solidification can use cloth or paper towel wipe, after curing must use scraper scrape scrub or xylene, acetone and other solvents.
7, note: acidity glass glue in curing process will release the excitant gas, to the person's eyes and respiratory stimulating role. Alcohol based neutral in the process of curing release methanol. Methanol has potential risk of cancer, and is known to skin and respiratory irritation, volatile gas can make the eyes, nose and throat inflammation. So should use this product in a well-ventilated environment, avoid getting into eyes or contact with the skin for a long time (after use, should wash your hands before eating, smoking), shall not be pharynx into this product. Don't let the children touch; Construction site should be well ventilated; Such as the eyes carelessly, application of water, and seek medical advice immediately. Fully cured glass glue, no any danger.
8, general guidelines: before use, please read carefully the glass glue construction method and use correctly, please note that for safe use and the related health hazard to the body.
9, about a two-component polysulfide sealant building:
A two-component polysulfide sealant is a liquid rubber as the main basic material, adding a variety of chemical agents through special polymer material synthesis process, is a novel non-toxic waterproof sealing material, the product has excellent water resistance, oil resistance, ageing resistance, corrosion resistance properties. And with good sealing, strong cohesive force, good elasticity and long service life.
10, polysulfide sealant building notice:
1) the applicable period: two-component polysulfide sealant building a, group b after mixing, the mixture has thickened gradually, exceed the applicable period will not be able to use. When using the environment temperature on the curing sealant considerable effect, the higher the temperature the shorter the applicable period, curing speed slow, when the temperature is too low, construction temperature with 5 ℃ ~ 35 ℃ advisable.
2) when using, sealing materials to the appropriate proportion of wide and deep.
3) the polysulfide sealant building storage to avoid the sun, appropriate is put in a cool and dry place. In 5 ~ 26 ℃ ambient temperature can be stored for half a year, time is too long will affect the use and physical properties. Such as: SS521 is single component, neutral curing, designed for glass, aluminum curtain wall and glass daylighting roof and metal structural engineering structural adhesive seal designed silicone sealant structure, excellent bonding performance of structure and the weathering resistance, after artificial accelerated weathering test, various physical and chemical properties have no obvious change in the sealant. Use glue gun to glue from the sealant tube into need bonded seal parts, seal to absorb the moisture in air at room temperature, curing as elastomer, an effective seal. General features: single component, neutral curing, for metal, no corrosive coated glass; Excellent weathering resistance, ageing resistance, uv resistance, ozone resistance, water resistance; High and low temperature resistant performance is remarkable, in - 30 ℃ ~ 90 ℃ range performance changed little; For most of building materials have excellent bonding; With other neutral silicone rubber with good compatibility. Main use: glass, aluminum curtain wall and glass daylighting roof and metal structural engineering structural adhesive seal; Hollow glass 2 bonded seal.
This article provided by OKorder building material online , reproduced please indicate:http://www.okorder.com/
2, sticking to the time: silicone rubber curing process is from the surface to inner development, different characteristics of the silicone table dry time and curing time is different (details please refer to the fourth article of curing time of the technical parameters of content), so if you want to repair was carried out on the surface must be conducted before the glass glue dry table (acid gel, neutral cellophane tape shall generally be in 5 to 10 minutes, neutral mixed glue shall generally be in 30 minutes). If the color paper to cover a certain place, glue, must be removed before epithelialization.
3, cure time: glass adhesive curing time is as the adhesive thickness increases, such as 12 mm thickness of acidity glass glue, may take 3 to 4 days can be solidified, but about 24 hours, have 3 mm outer layer has formed. Most bonding glass, metal or wood, after 72 hours at room temperature is 20 pounds per inch of the peel strength. If use some or all of the sealed glass glue, so, cure time is determined by the degree of closed tightly. In absolute airtight place, it may never keep curing. If the temperature will make glass glue is soft. Metal and metal bonding gap should not be more than 25 mm below. In all kinds of adhesive, including closed cases, after bonding equipment before use, should be fully check the bonding effect.
Acidity glass glue in the process of solidification, due to the volatilization of acetic acid will produce a taste, the taste will disappear in the process of curing, after curing will no peculiar smell.
4, adhesive: a. wiping the metal and plastic surface completely, degreasing, then in addition to plastic surface with acetone rinse all first, rubber surface application of sand paper burnish, then wipe with acetone. The use of acetone please abide by the use of the matters needing attention of the solvent. B. glass glue evenly coated on the surface of the object that is ready, if is two surface bonding, can put a look for the position, the other side extrusion with enough force to squeeze out the air, but be careful not to squeeze out the glass glue. C. puts the device of the adhesive at room temperature, glass glue curing.
5, seal: to use silicone glass glue sealing occasions, also carried out in accordance with the above steps, glass glue hard into joint or crack, make good contact with glass glue and surface.
6, cleaning: glass glue before solidification can use cloth or paper towel wipe, after curing must use scraper scrape scrub or xylene, acetone and other solvents.
7, note: acidity glass glue in curing process will release the excitant gas, to the person's eyes and respiratory stimulating role. Alcohol based neutral in the process of curing release methanol. Methanol has potential risk of cancer, and is known to skin and respiratory irritation, volatile gas can make the eyes, nose and throat inflammation. So should use this product in a well-ventilated environment, avoid getting into eyes or contact with the skin for a long time (after use, should wash your hands before eating, smoking), shall not be pharynx into this product. Don't let the children touch; Construction site should be well ventilated; Such as the eyes carelessly, application of water, and seek medical advice immediately. Fully cured glass glue, no any danger.
8, general guidelines: before use, please read carefully the glass glue construction method and use correctly, please note that for safe use and the related health hazard to the body.
9, about a two-component polysulfide sealant building:
A two-component polysulfide sealant is a liquid rubber as the main basic material, adding a variety of chemical agents through special polymer material synthesis process, is a novel non-toxic waterproof sealing material, the product has excellent water resistance, oil resistance, ageing resistance, corrosion resistance properties. And with good sealing, strong cohesive force, good elasticity and long service life.
10, polysulfide sealant building notice:
1) the applicable period: two-component polysulfide sealant building a, group b after mixing, the mixture has thickened gradually, exceed the applicable period will not be able to use. When using the environment temperature on the curing sealant considerable effect, the higher the temperature the shorter the applicable period, curing speed slow, when the temperature is too low, construction temperature with 5 ℃ ~ 35 ℃ advisable.
2) when using, sealing materials to the appropriate proportion of wide and deep.
3) the polysulfide sealant building storage to avoid the sun, appropriate is put in a cool and dry place. In 5 ~ 26 ℃ ambient temperature can be stored for half a year, time is too long will affect the use and physical properties. Such as: SS521 is single component, neutral curing, designed for glass, aluminum curtain wall and glass daylighting roof and metal structural engineering structural adhesive seal designed silicone sealant structure, excellent bonding performance of structure and the weathering resistance, after artificial accelerated weathering test, various physical and chemical properties have no obvious change in the sealant. Use glue gun to glue from the sealant tube into need bonded seal parts, seal to absorb the moisture in air at room temperature, curing as elastomer, an effective seal. General features: single component, neutral curing, for metal, no corrosive coated glass; Excellent weathering resistance, ageing resistance, uv resistance, ozone resistance, water resistance; High and low temperature resistant performance is remarkable, in - 30 ℃ ~ 90 ℃ range performance changed little; For most of building materials have excellent bonding; With other neutral silicone rubber with good compatibility. Main use: glass, aluminum curtain wall and glass daylighting roof and metal structural engineering structural adhesive seal; Hollow glass 2 bonded seal.
This article provided by OKorder building material online , reproduced please indicate:http://www.okorder.com/